solution strengthening

this can be attributed to the strengthening effect of bi from solid solution strengthening to precipitating strengthening in the solders.

这可归因于Bi的固溶强化与弥散强化作用的转化。

it is thought that solution strengthening and second phase strengthening are two main ways for improving mechanical properties of magnesium alloy.

认为固溶强化和第二相强化是加入合金元素强化镁合金的主要方式。

it was found from the auger analysis that the concentrations of c and v were 50% and 30% respectively, and therefore the solid solution strengthening appeared.

俄歇分析表明C、V离子注入浓度将分别达到50%和30%的原子比例，即形成固溶强化。

Development and property analysis of ultra-low carbon self-shielded flux-cored wire with nitride solid solution strengthening

超低碳氮强化自保护药芯焊丝的研制及性能分析

a study on solid solution strengthening of w-ni-cu heavy alloy

W-N-Cu重合金固溶强化的机理研究

This is a solid solution strengthening effect reflected in the valence electron structure.

这是固溶强化效果在价电子结构中的反映。

Micro-hardness test and XRD spectra indicate that artificial ageing treatment at low temperature can further improve the mechanical property of the solid solution strengthening aluminum alloy after ECAP process.

显微硬度以及XRD测试结果显示低温时效处理进一步提高了强化固溶态高强铝合金ECAP加工后的机械力学性能。

it is also interestingly found that cu-p alloys with addition of 3% ni possess the lowest hardness value which is caused by the combined effect of eutectic deviation and weak solid solution strengthening due to the addition of ni.

当向Cu-8P合金中加入3%的Ni时，合金的硬度值达到最小值，这是由于合金成分偏离共晶成分且Ni的固溶强化作用比较微弱的综合效果。

solution treatment can increase solute atoms in the matrix and improve the tensile properties of as cast alloy owing to the better solid solution strengthening effect, but the solution treatment deteriorates the tensile properties of extruded alloys as the result of the grain growth.

固溶处理可以使合金中的溶质原子增加而产生更好的固溶强化作用，提高了铸态合金的拉伸性能，但固溶处理使挤压态合金中晶粒过分长大，降低了合金拉伸性能。

when the nb content in hp alloy containing 0.4 wt% c is less than 0.5 wt%, the nb exists in the matrix and mainly plays the part of solution strengthening.

在含碳0.4（wt%）的HP合金中添加0.5（wt%）以下的Nb，主要起固溶强化作用；

The experimental results show that Ti and Zr are mainly functioned as solution strengthening elements.

研究结果表明：合金化元素钛、锆对合金主要是起固溶强化作用。

The improvement of YTS is attributed to the grain refinement strengthening of Y and Zn, and to the solid solution strengthening of Zn. The reduction of UTS and elongation are caused by the precipitation of a compound phase along the grain boundary.

Y、Zn元素的细晶强化及Zn元素的固溶强化是屈服强度提高的主要原因；抗拉强度和延伸率的降低是由于化合物相沿晶界析出。

Solid solution strengthening for MIM Fe-based alloys

MIM Fe基合金的固溶强化

the dissolution of the intermetallic phases was studied and the function of solution strengthening in al-si-cu-mg casting alloys during solution heat treatment was analyzed.

对固溶处理过程中铸造Al-Si-Cu-Mg合金析出相溶解过程进行了研究。

under the condition of this thesis, the strengthening mechanism of the above alloy mainly includes solution strengthening, deformation strengthening and aging strengthening.

在本论文研究条件下，合金的强化机制为固溶强化、形变强化和时效析出强化。

as compared with solution strengthening of aluminum, the dispersion strengthening of alumina improved obviously not only electric conductivity but also hardness of the material.

与Al的固溶强化相比，Al2O3粒子的弥散强化不仅大大提高了电导率，而且显著提高了材料的硬度。

theoretical analyses have shown that boron benefits precipitation strengthening, solution strengthening and grain boundary strengthening.

理论分析表明：硼对沉淀强化、固溶强化和晶界强化均有贡献。

it discusses the strengthening mechanism of addition elements on silver alloy in the aspects of solution strengthening, the fine-grained strengthening, the ageing strengthening and second-phase strengthening, and makes research on how addition elements affect the properties of resistance to natural ageing and anti-tarnishing.

从固溶强化、细晶强化、时效强化和第二相强化等方面讨论了银合金添加元素的强化机理，以及添加元素对抗自然时效和抗变色能力的影响。

low carbon martensitic steel has high strength because of the effect of carbon solution strengthening and dislocation strengthening.

低碳马氏体钢由于碳的固溶强化、位错强化等作用通常具有较高的强度。